SABIC Innovative Plastics Valox? 553 PBT+PC
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Specific Gravity比重
|
1.59 g/cc
|
1.59 g/cc
|
ASTM D 792
|
|
Water Absorption吸水率
|
0.070 %
@Time 86400 sec |
0.070 %
@Time 24.0 hour |
ASTM D 570
|
|
Linear Mold Shrinkage, Flow線性收縮率/流動
|
0.0030 - 0.0050 cm/cm
@Thickness 1.50 - 3.20 mm |
0.0030 - 0.0050 in/in
@Thickness 0.0591 - 0.126 in |
SABIC Method
|
|
0.0050 - 0.0080 cm/cm
@Thickness 3.20 - 4.60 mm |
0.0050 - 0.0080 in/in
@Thickness 0.126 - 0.181 in |
SABIC Method
|
|
|
Linear Mold Shrinkage, Transverse線性收縮率/橫向
|
0.0040 - 0.0060 cm/cm
@Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in
@Thickness 0.0591 - 0.126 in |
SABIC Method
|
|
0.0060 - 0.0090 cm/cm
@Thickness 3.20 - 4.60 mm |
0.0060 - 0.0090 in/in
@Thickness 0.126 - 0.181 in |
SABIC Method
|
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Hardness, Rockwell R羅氏硬度R
|
118
|
118
|
ASTM D 785
|
|
Tensile Strength at Break斷裂拉伸強度
|
110 MPa
|
16000 psi
|
Type I, 5 mm/min; ASTM D 638
|
|
Flexural Strength彎曲強度
|
179 MPa
|
26000 psi
|
brk, 1.3 mm/min, 50 mm span; ASTM D 790
|
|
Flexural Modulus彎曲彈性模量
|
6.89 GPa
|
999 ksi
|
1.3 mm/min, 50 mm span; ASTM D 790
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度
|
0.850 J/cm
@Temperature 23.0 °C |
1.59 ft-lb/in
@Temperature 73.4 °F |
ASTM D 256
|
|
Izod Impact, Unnotched懸臂梁無缺口沖擊強度
|
6.40 J/cm
@Temperature 23.0 °C |
12.0 ft-lb/in
@Temperature 73.4 °F |
ASTM D 4812
|
|
Electrical Properties電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
4.30e+16 ohm-cm
|
4.30e+16 ohm-cm
|
ASTM D 257
|
|
Dielectric Constantt介電常數
|
3.7
@Frequency 1.00e+6 Hz |
3.7
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
3.8
@Frequency 100 Hz |
3.8
@Frequency 100 Hz |
ASTM D 150
|
|
|
Dielectric Strength介電強度
|
18.8 kV/mm
@Thickness 3.20 mm |
478 kV/in
@Thickness 0.126 in |
in air; ASTM D 149
|
|
25.5 kV/mm
@Thickness 1.60 mm |
648 kV/in
@Thickness 0.0630 in |
in oil; ASTM D 149
|
|
|
Dissipation Factor耗散因數
|
0.0020
@Frequency 100 Hz |
0.0020
@Frequency 100 Hz |
ASTM D 150
|
|
0.020
@Frequency 1.00e+6 Hz |
0.020
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
|
Arc Resistance 耐電弧性
|
60 - 120 sec
|
60 - 120 sec
|
Tungsten, PLC code 6; ASTM D 495
|
|
Comparative Tracking Index相對漏電起痕指數
|
175 - 250 V
|
175 - 250 V
|
PLC code 3; UL 746A
|
|
Hot Wire Ignition, HWI熱線圈點燃測試
|
60 - 120 sec
|
60 - 120 sec
|
PLC code 1; UL 746A
|
|
High Amp Arc Ignition, HAI高電流電弧點燃測試
|
15 - 30 arcs
|
15 - 30 arcs
|
surface, PLC code 3; UL 746A
|
|
High Voltage Arc-Tracking Rate, HVTR高壓電弧跟蹤速度
|
80.0 - 150 mm/min
|
3.15 - 5.91 in/min
|
PLC code 3; UL 746A
|
|
Thermal Properties熱性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
CTE, linear, Parallel to Flow線性熱膨脹系數
|
21.6 μm/m-°C
@Temperature -40.0 - 40.0 °C |
12.0 μin/in-°F
@Temperature -40.0 - 104 °F |
ASTM E 831
|
|
21.6 μm/m-°C
@Temperature 60.0 - 138 °C |
12.0 μin/in-°F
@Temperature 140 - 280 °F |
ASTM E 831
|
|
|
Deflection Temperature at熱變形溫度0.46 MPa (66 psi)
|
204 °C
@Thickness 6.40 mm |
399 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
160 °C
@Thickness 6.40 mm |
320 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
UL RTI, Electrical相對溫度指數
|
125 °C
|
257 °F
|
UL 746B
|
|
UL RTI, Mechanical with Impact機械沖擊熱指數
|
110 °C
|
230 °F
|
UL 746B
|
|
UL RTI, Mechanical without Impact無機械沖擊熱指數
|
125 °C
|
257 °F
|
UL 746B
|
|
Flammability, UL94阻燃等級
|
V-0
@Thickness 0.860 mm |
V-0
@Thickness 0.0339 in |
UL 94
|
|
5VA
@Thickness 2.31 mm |
5VA
@Thickness 0.0909 in |
UL 94
|
|
|
Oxygen Index氧指數
|
37.1 %
|
37.1 %
|
LOI; ASTM D 2863
|
PBT 現貨 加纖30% 基礎創新（GE) 553 量大優惠