SABIC沙伯基礎(chǔ)創(chuàng)新塑料PBT Valox 357物性參數(shù)物性表
以下是SABIC沙伯基礎(chǔ)創(chuàng)新塑料PBT Valox 357的中英文物性表
|
SABIC Innovative Plastics Valox? 357 PBT
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質(zhì)
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
Density密度
|
1.34 g/cc
|
0.0484 lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
0.080 %
@Time 86400 sec |
0.080 %
@Time 24.0 hour |
ASTM D 570
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
0.15 %
|
0.15 %
|
23°C / 50% RH; ISO 62
|
|
Water Absorption吸水率 at Saturation
|
0.50 %
@Temperature 23.0 °C |
0.50 %
@Temperature 73.4 °F |
ISO 62
|
|
Linear Mold Shrinkage, Flow線性收縮率/流動
|
0.0080 - 0.011 in/in
@Thickness 0.0295 - 0.0906 in |
SABIC Method
|
|
|
0.010 - 0.014 cm/cm
@Thickness 2.30 - 4.60 mm |
0.010 - 0.014 in/in
@Thickness 0.0906 - 0.181 in |
SABIC Method
|
|
|
0.010 - 0.014 cm/cm
@Thickness 3.20 mm |
0.010 - 0.014 in/in
@Thickness 0.126 in |
SABIC Method
|
|
|
Linear Mold Shrinkage, Transverse線性收縮率/橫向
|
0.0090 - 0.013 cm/cm
@Thickness 0.750 - 2.30 mm |
0.0090 - 0.013 in/in
@Thickness 0.0295 - 0.0906 in |
SABIC Method
|
|
0.012 - 0.016 cm/cm
@Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in
@Thickness 0.0906 - 0.181 in |
SABIC Method
|
|
|
Melt Flow熔體流動速率
|
8.0 g/10 min
@Load 5.00 kg, Temperature 250 °C |
8.0 g/10 min
@Load 11.0 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133
|
|
9.6 g/10 min
@Load 5.00 kg, Temperature 250 °C |
9.6 g/10 min
@Load 11.0 lb, Temperature 482 °F |
ASTM D 1238
|
|
|
Mechanical Properties力學(xué)性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
Hardness, Rockwell R羅氏硬度R
|
117
|
117
|
ASTM D 785
|
|
Tensile Strength at Break斷裂拉伸強度
|
40.0 MPa
|
5800 psi
|
50 mm/min; ISO 527
|
|
42.0 MPa
|
6090 psi
|
Type I, 50 mm/min; ASTM D 638
|
|
|
Tensile Strength, Yield屈服拉伸強度
|
48.0 MPa
|
6960 psi
|
Type I, 50 mm/min; ASTM D 638
|
|
50.0 MPa
|
7250 psi
|
50 mm/min; ISO 527
|
|
|
Elongation at Break斷裂伸長率
|
30 %
|
30 %
|
50 mm/min; ISO 527
|
|
54 %
|
54 %
|
Type I, 50 mm/min; ASTM D 638
|
|
|
Elongation at Yield屈服伸長率
|
5.0 %
|
5.0 %
|
Type I, 50 mm/min; ASTM D 638
|
|
5.0 %
|
5.0 %
|
50 mm/min; ISO 527
|
|
|
Tensile Modulus拉伸模量
|
2.02 GPa
|
293 ksi
|
5 mm/min; ASTM D 638
|
|
2.20 GPa
|
319 ksi
|
1 mm/min; ISO 527
|
|
|
Flexural Strength
|
78.0 MPa
|
11300 psi
|
brk, 1.3 mm/min, 50 mm span; ASTM D 790
|
|
Flexural Yield Strength彎曲屈服強度
|
73.0 MPa
|
10600 psi
|
2 mm/min; ISO 178
|
|
78.0 MPa
|
11300 psi
|
1.3 mm/min, 50 mm span; ASTM D 790
|
|
|
Flexural Modulus彎曲彈性模量
|
2.00 GPa
|
290 ksi
|
2 mm/min; ISO 178
|
|
2.10 GPa
|
305 ksi
|
1.3 mm/min, 50 mm span; ASTM D 790
|
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度
|
1.53 J/cm
@Temperature -30.0 °C |
2.87 ft-lb/in
@Temperature -22.0 °F |
ASTM D 256
|
|
3.19 J/cm
@Temperature 23.0 °C |
5.98 ft-lb/in
@Temperature 73.4 °F |
ASTM D 256
|
|
|
Izod Impact, Unnotched懸臂梁無缺口沖擊強度
|
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
ASTM D 4812
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度 (ISO)
|
10.0 kJ/m2
@Temperature -30.0 °C |
4.76 ft-lb/in2
@Temperature -22.0 °F |
80*10*4; ISO 180/1A
|
|
45.0 kJ/m2
@Temperature 23.0 °C |
21.4 ft-lb/in2
@Temperature 73.4 °F |
80*10*4; ISO 180/1A
|
|
|
Charpy Impact, Notched夏比缺口沖擊
|
4.50 J/cm2
@Temperature 23.0 °C |
21.4 ft-lb/in2
@Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
|
|
Gardner Impact加德納的影響
|
43.0 J
@Temperature 23.0 °C |
31.7 ft-lb
@Temperature 73.4 °F |
ASTM D 3029
|
|
43.0 J
@Temperature 23.0 °C |
31.7 ft-lb
@Temperature 73.4 °F |
ASTM D 3029
|
|
|
Impact Test沖擊試驗數(shù)據(jù)
|
35.0 J
@Temperature 23.0 °C |
25.8 ft-lb
@Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763
|
|
Electrical Properties電性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
>= 1.20e+16 ohm-cm
|
>= 1.20e+16 ohm-cm
|
ASTM D 257
|
|
Dielectric Constant介電常數(shù)
|
3.2
@Frequency 100 Hz |
3.2
@Frequency 100 Hz |
ASTM D 150
|
|
3.2
@Frequency 1.00e+6 Hz |
3.2
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
|
Dielectric Strength介電強度
|
18.5 kV/mm
@Thickness 3.20 mm |
470 kV/in
@Thickness 0.126 in |
in air; ASTM D 149
|
|
18.5 kV/mm
@Thickness 3.20 mm |
470 kV/in
@Thickness 0.126 in |
in oil; ASTM D 149
|
|
|
25.2 kV/mm
@Thickness 1.60 mm |
640 kV/in
@Thickness 0.0630 in |
in oil; ASTM D 149
|
|
|
Dissipation Factor耗散因數(shù)
|
0.0030
@Frequency 100 Hz |
0.0030
@Frequency 100 Hz |
ASTM D 150
|
|
0.030
@Frequency 1.00e+6 Hz |
0.030
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
|
Arc Resistance 耐電弧性
|
60 - 120 sec
|
60 - 120 sec
|
Tungsten, PLC code 6; ASTM D 495
|
|
Comparative Tracking Index相對漏電起痕指數(shù)
|
250 - 400 V
|
250 - 400 V
|
PLC code 2; UL 746A
|
|
Hot Wire Ignition, HWI熱線圈點燃測試
|
30 - 60 sec
|
30 - 60 sec
|
PLC code 2; UL 746A
|
|
High Amp Arc Ignition, HAI高電流電弧點燃測試
|
15 - 30 arcs
|
15 - 30 arcs
|
surface, PLC code 3; UL 746A
|
|
High Voltage Arc-Tracking Rate, HVTR高壓電弧跟蹤速度
|
80.0 - 150 mm/min
|
3.15 - 5.91 in/min
|
PLC code 3; UL 746A
|
|
Thermal Properties熱性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
CTE, linear, Parallel to Flow線性熱膨脹系數(shù)
|
72.0 μm/m-°C
@Temperature -40.0 - 40.0 °C |
40.0 μin/in-°F
@Temperature -40.0 - 104 °F |
ISO 11359-2
|
|
91.8 μm/m-°C
@Temperature -40.0 - 40.0 °C |
51.0 μin/in-°F
@Temperature -40.0 - 104 °F |
ASTM E 831
|
|
|
124 μm/m-°C
@Temperature 60.0 - 138 °C |
68.9 μin/in-°F
@Temperature 140 - 280 °F |
ASTM E 831
|
|
|
CTE, linear, Transverse to Flow線性熱膨脹系數(shù)/橫向
|
84.0 μm/m-°C
@Temperature -40.0 - 40.0 °C |
46.7 μin/in-°F
@Temperature -40.0 - 104 °F |
ASTM E 831
|
|
84.0 μm/m-°C
@Temperature -40.0 - 40.0 °C |
46.7 μin/in-°F
@Temperature -40.0 - 104 °F |
ISO 11359-2
|
|
|
Deflection Temperature at熱變形溫度0.46 MPa (66 psi)
|
135 °C
@Thickness 3.20 mm |
275 °F
@Thickness 0.126 in |
unannealed; ASTM D 648
|
|
138 °C
@Thickness 6.40 mm |
280 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
84.0 °C
|
183 °F
|
Flatw 80*10*4 sp=64mm; ISO 75/Af
|
|
98.0 °C
@Thickness 3.20 mm |
208 °F
@Thickness 0.126 in |
unannealed; ASTM D 648
|
|
|
99.0 °C
@Thickness 6.40 mm |
210 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
|
Vicat Softening Point維卡軟化點
|
134 °C
|
273 °F
|
Rate B/50; ASTM D 1525
|
|
145 °C
|
293 °F
|
Rate B/50; ISO 306
|
|
|
150 °C
|
302 °F
|
Rate B/120; ISO 306
|
|
|
UL RTI, Electrical相對溫度指數(shù)
|
120 °C
|
248 °F
|
UL 746B
|
|
UL RTI, Mechanical with Impact機械沖擊熱指數(shù)
|
120 °C
|
248 °F
|
UL 746B
|
|
UL RTI, Mechanical without Impact無機械沖擊熱指數(shù)
|
140 °C
|
284 °F
|
UL 746B
|
|
Flammability, UL94阻燃等級
|
HB
@Thickness 0.450 mm |
HB
@Thickness 0.0177 in |
UL 94
|
|
V-0
@Thickness 0.630 mm |
V-0
@Thickness 0.0248 in |
UL 94
|
|
|
5VA
@Thickness 3.00 mm |
5VA
@Thickness 0.118 in |
UL 94
|
|
|
Oxygen Index氧指數(shù)
|
30 %
|
30 %
|
LOI; ASTM D 2863
|