以下是BASF PA66 Ultramid A3EG6中英文物性表
|
BASF Ultramid? A3EG6 PA66(尼龍66-聚酰胺)
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Density密度
|
1.36 g/cc
|
0.0491 lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
5.2 - 5.8 %
|
5.2 - 5.8 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
1.5 - 1.9 %
|
1.5 - 1.9 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Test粘度
|
145 cm3/g
|
145 cm3/g
|
Viscosity number
|
|
Linear Mold Shrinkage線性收縮率
|
0.0055 cm/cm
|
0.0055 in/in
|
|
|
Melt Flow熔體流動速率
|
54.4 g/10 min
@Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Tensile Strength, Yield屈服拉伸強度
|
190 MPa
|
27600 psi
|
ISO 527
|
|
Elongation at Yield屈服伸長率
|
3.0 %
|
3.0 %
|
ISO 527
|
|
Modulus of Elasticity彈性模量
|
10.0 GPa
|
1450 ksi
|
|
|
Flexural Strength彎曲強度
|
280 MPa
|
40600 psi
|
iso 178
|
|
Flexural Modulus彎曲彈性模量
|
8.60 GPa
|
1250 ksi
|
ISO 178
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度 (ISO)
|
11.5 kJ/m2
|
5.47 ft-lb/in2
|
ISO 180/A
|
|
Charpy Impact Unnotched夏比缺口試樣沖擊
|
8.50 J/cm2
|
40.5 ft-lb/in2
|
ISO 179/1eU
|
|
7.00 J/cm2
@Temperature -30.0 °C |
33.3 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eU
|
|
|
Charpy ImPAct, Notched夏比缺口沖擊
|
1.30 J/cm2
|
6.19 ft-lb/in2
|
ISO 179/1eA
|
|
1.00 J/cm2
@Temperature -30.0 °C |
4.76 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eA
|
|
|
Electrical Properties電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
1.00e+13 ohm-cm
|
1.00e+13 ohm-cm
|
IEC 60093
|
|
Dielectric Constant 介電常數
|
3.5
@Frequency 1.00e+6 Hz |
3.5
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
Dissipation Factor 耗散因數
|
0.014
@Frequency 1.00e+6 Hz |
0.014
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
Comparative Tracking Index 跟蹤指數
|
550 V
|
550 V
|
IEC 60112
|
|
Thermal Properties熱性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
CTE, linear, Parallel to Flow線性熱膨脹系數
|
0.200 - 0.300 μm/m-°C
@Temperature 23.0 - 80.0 °C |
0.111 - 0.167 μin/in-°F
@Temperature 73.4 - 176 °F |
ISO 11359
|
|
CTE, linear, Transverse to Flow線性熱膨脹系數/橫向
|
0.600 - 0.700 μm/m-°C
@Temperature 23.0 - 80.0 °C |
0.333 - 0.389 μin/in-°F
@Temperature 73.4 - 176 °F |
ISO 11359
|
|
Specific Heat Capacity比熱容
|
1.50 J/g-°C
|
0.359 BTU/lb-°F
|
|
|
Thermal Conductivity導熱系數
|
0.350 W/m-K
|
2.43 BTU-in/hr-ft2-°F
|
DIN 52612
|
|
Melting Point熔點
|
260 °C
|
500 °F
|
DIN 53765
|
|
Maximum Service Temperature, Air使用溫度
|
240 °C
|
464 °F
|
ISO 527
|
|
Deflection Temperature at熱變形溫度0.46 MPa (66 psi)
|
250 °C
|
482 °F
|
ISO 75
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
250 °C
|
482 °F
|
ISO 75
|
|
Flammability, UL94阻燃等級
|
HB
@Thickness 1.60 mm |
HB
@Thickness 0.0630 in |
|
|
Processing Properties加工性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Melt Temperature熔體溫度
|
280 - 300 °C
|
536 - 572 °F
|
|
|
Mold Temperature模具溫度
|
80.0 - 90.0 °C
|
176 - 194 °F
|
|