以下是BASF PA66 Ultramid A3EG3中英文物性表
|
BASF Ultramid? A3EG3 PA66(尼龍66-聚酰胺)
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Density密度
|
1.24 g/cc
|
0.0448 lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
7.0 %
|
7.0 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
2.2 %
|
2.2 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Test粘度
|
145 cm3/g
|
145 cm3/g
|
Viscosity number
|
|
Linear Mold Shrinkage線性收縮率
|
0.0055 cm/cm
|
0.0055 in/in
|
ASTM Data; MD
|
|
Melt Flow熔體流動速率
|
70 g/10 min
@Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Tensile Strength at Break斷裂拉伸強度
|
114 MPa
|
16500 psi
|
0.2 in/min; ASTM Test
|
|
156 MPa
@Temperature -40.0 °C |
22600 psi
@Temperature -40.0 °F |
ISO Data
|
|
|
Tensile Strength, Ultimate極限拉伸強度
|
130 MPa
|
18900 psi
|
5mm/min; ISO 527
|
|
Tensile Strength, Yield屈服拉伸強度
|
74.0 MPa
@Temperature 80.0 °C |
10700 psi
@Temperature 176 °F |
ISO Data
|
|
Elongation at Break斷裂伸長率
|
3.0 %
|
3.0 %
|
5mm/min; ISO 527
|
|
3.0 %
|
3.0 %
|
0.2 in/min; ASTM Test
|
|
|
2.6 %
@Temperature -40.0 °C |
2.6 %
@Temperature -40.0 °F |
ISO Data
|
|
|
Elongation at Yield屈服伸長率
|
7.4 %
@Temperature 80.0 °C |
7.4 %
@Temperature 176 °F |
ISO Data
|
|
Tensile Modulus拉伸模量
|
5.86 GPa
|
850 ksi
|
ASTM Test
|
|
6.00 GPa
|
870 ksi
|
1mm/min; ISO 527
|
|
|
Flexural Strength彎曲強度
|
180 MPa
|
26100 psi
|
ISO Data
|
|
Flexural Modulus彎曲彈性模量
|
5.17 GPa
|
750 ksi
|
ASTM Test
|
|
5.20 GPa
|
754 ksi
|
ISO Data
|
|