點(diǎn)擊圖片查看大圖現(xiàn)貨PET 杜邦 Rynite FR543 NC010 防火玻纖增強(qiáng)43PET
Rynite® FR543 NC010
THERMOPLASTIC POLYESTER RESIN
PET-GF43 FR(17)
CHARACTERISTICS
Processing
Injection Molding
Delivery form
Pellets
Additives
Release agent, Flame retardant
Special characteristics
Flame retardant
PRODUCT TEXT
Rynite® FR543 NC010 is a 43% Glass Reinforced, Flame Retardant, Polyethylene Terephthalate
PRODUCT INFORMATION
VALUE
TEST NORM
Resin Identification
PET-GF43FR(17)
ISO 1043
Part Marking Code
>PET-GF43FR(17)<
ISO 11469
RHEOLOGICAL PROPERTIES
VALUE
UNIT
TEST NORM
Molding shrinkage, parallel
0.2
%
ISO 294-4, 2577
Molding shrinkage, normal
0.8
%
ISO 294-4, 2577
Postmolding shrinkage, normal, 48h at 175°F
0.35
%
ISO 294-4
Postmolding shrinkage, parallel, 48h at 175°F
0.05
%
ISO 294-4
MECHANICAL PROPERTIES
VALUE
UNIT
TEST NORM
Tensile Modulus
17000
MPa
ISO 527-1/-2
Stress at break
170
MPa
ISO 527-1/-2
Strain at break
1.8
%
ISO 527-1/-2
Flexural Modulus
14500
MPa
ISO 178
Compressive strength
230
MPa
ISO 604
Shear Strength
60
MPa
ASTM D 732
Tensile creep modulus, 1000h
15000
MPa
ISO 899-1
Charpy impact strength, 73°F
43
kJ/m2
ISO 179/1eU
Charpy impact strength, -22°F
30
kJ/m2
ISO 179/1eU
Charpy notched impact strength, 73°F
10
kJ/m2
ISO 179/1eA
Charpy notched impact strength, -22°F
10
kJ/m2
ISO 179/1eA
Hardness, Rockwell, M-scale
102
-
ISO 2039-2
Hardness, Rockwell, R-scale
122
-
ISO 2039-2
Poisson's ratio
0.33
-
-
TRIBOLOGICAL PROPERTIES
VALUE
TEST NORM
Coefficient of static friction, against itself
0.18
ASTM 1894
Coefficient of static friction, against steel
0.16
ASTM 1894
THERMAL PROPERTIES
VALUE
UNIT
TEST NORM
Melting temperature, 18°F/min
254
°C
ISO 11357-1/-3
Temp. of deflection under load, 260 psi
225
°C
ISO 75-1/-2
Temp. of deflection under load, 65 psi
240
°C
ISO 75-1/-2
Vicat softening temperature, 90°F/h, 11 lbf
225
°C
ISO 306
Coeff. of linear therm. expansion, parallel
10
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, normal
80
E-6/K
ISO 11359-1/-2
Coeff. of linear therm. expansion, Normal,23-55°C (73-130°F)
79
E-6/K
ASTM E 831
Coeff. of linear therm. expansion, Parallel, 23-55°C(73-130°F)
11
E-6/K
ASTM E 831
Thermal conductivity solid
0.31
W/(m K)
-
Thermal conductivity of melt
0.3
W/(m K)
-
Spec. heat capacity of melt
1560
J/(kg K)
-
RTI, electrical, 30mil
155
°C
UL 746B
RTI, electrical, 60mil
155
°C
UL 746B
RTI, electrical, 120mil
155
°C
UL 746B
RTI, impact, 30mil
155
°C
UL 746B
RTI, impact, 60mil
155
°C
UL 746B
RTI, impact, 120mil
155
°C
UL 746B
RTI, strength, 30mil
155
°C
UL 746B
RTI, strength, 60mil
155
°C
UL 746B
RTI, strength, 120mil
155
°C
UL 746B
FLAMMABILITY
VALUE
UNIT
TEST NORM
Burning Behav. at 60mil nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. at thickness h
V-0
class
IEC 60695-11-10
Thickness tested
0.8
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. 5V at thickness h
5VA
class
IEC 60695-11-20
Thickness tested
1.5
mm
IEC 60695-11-20
UL recognition
yes
-
UL 94
Oxygen index
35
%
ISO 4589-1/-2
Glow Wire Flammability Index, 120mil
960
°C
IEC 60695-2-12
Glow Wire Ignition Temperature, 120mil
960
°C
IEC 60695-2-13
Glow Wire Temperature, No Flame, 30mil
960
°C
IEC 60335-1
Glow Wire Temperature, No Flame, 40mil
960
°C
IEC 60335-1
Glow Wire Temperature, No Flame, 60mil
960
°C
IEC 60335-1
Glow Wire Temperature, No Flame, 80mil
960
°C
IEC 60335-1
Glow Wire Temperature, No Flame, 120mil
960
°C
IEC 60335-1
FMVSS Class
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
<80
mm/min
ISO 3795 (FMVSS 302)
ELECTRICAL PROPERTIES
VALUE
UNIT
TEST NORM
Relative permittivity, 100Hz
4.6
-
IEC 62631-2-1
Relative permittivity, 1MHz
4.1
-
IEC 62631-2-1
Dissipation factor, 100Hz
368
E-4
IEC 62631-2-1
Dissipation factor, 1MHz
131
E-4
IEC 62631-2-1
Volume resistivity
>1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
1E15
Ohm
IEC 62631-3-2
Electric strength
37
kV/mm
IEC 60243-1
Comparative tracking index
225
-
IEC 60112
Comparative tracking index
2
PLC
UL 746A
OTHER PROPERTIES
VALUE
UNIT
TEST NORM
Humidity absorption, 80mil
0.1
%
Sim. to ISO 62
Water absorption, 80mil
0.6
%
Sim. to ISO 62
Density
1790
kg/m3
ISO 1183
Density of melt
1610
kg/m3
-
INJECTION
VALUE
UNIT
Drying Recommended
yes
Drying Temperature
120
°C
Drying Time, Dehumidified Dryer
4 - 6
h
Processing Moisture Content
≤0.021
%
Melt Temperature Optimum
280
°C
Min. melt temperature
270
°C
Max. melt temperature
290
°C
Max. screw tangential speed
0.2
m/s
Mold Temperature Optimum
110
°C
Min. mold temperature
100
°C
Max. mold temperature
1202
°C
Hold pressure range
≥80
MPa
Hold pressure time
4
s/mm
Back pressure
As low as possible
MPa
Ejection temperature
170
°C
1: At levels above 0.02%, strength and toughness will decrease, even though parts may not exhibit surface defects.
2: (6mm - 1mm thickness)
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。