LCP液晶聚合物 美國杜邦6330 30% 礦物填料 耐沖擊
產品參數
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.64 | ||
| 模具收縮率 | 3.2mm(0.126in) | ASTM D-955 | 0.5 | % | |
| 機械性能 | 彎曲強度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 125 | MPa |
| 斷裂伸長率 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 4 | % | |
| 彎曲模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 9600 | MPa | |
| 彎曲模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 9600 | MPa | |
| 彎曲模量 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 13900 | MPa | |
| 拉伸模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 11569 | MPa | |
| 拉伸強度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 141 | MPa | |
| 斷裂伸長率 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 3.3 | % | |
| 壓縮模量 | ASTM D-695 | 4100 | MPa | ||
| 彎曲強度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 125 | MPa | |
| IZOD沖擊強度 | 3.2mm(0.126in) | ASTM D-256 | 160 | J/m | |
| 斷裂伸長率 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 4 | % | |
| 拉伸模量 | 3.2mm | ASTM D-638 | 10500 | MPa | |
| 拉伸模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 11569 | MPa | |
| 壓縮模量 | ASTM D-695 | 4100 | MPa | ||
| 彎曲強度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 158 | MPa | |
| 彎曲模量 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 13900 | MPa | |
| 拉伸模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 10500 | MPa | |
| IZOD沖擊強度 | 3.2mm(0.126in) | ASTM D-256 | 160 | J/m | |
| 彎曲強度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 158 | MPa | |
| 拉伸強度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 125 | MPa | |
| 電氣性能 | 損耗因數 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 0.001 | |
| 損耗因數 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 0.002 | ||
| 介電強度 | 0.8mm | ASTM D-149 | 49 | Kv/mm | |
| 介電常數 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 3.9 | ||
| 介電常數 | 0.8mm(0.032in) | ASTM D-150 | 2.9 | ||
| 介電常數 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 4 | ||
| 損耗因數 | 0.8mm(0.032in) | ASTM D-150 | 0.013 | ||
| 介電強度 | 3.2mm | ASTM D-149 | 26 | Kv/mm | |
| 介電常數 | 0.8mm | ASTM D-150 | 3.3 | ||
| 介電常數 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 4.1 | ||
| 介電常數 | 3.2mm(0.125in) | ASTM D-150 | 3.6 | ||
| 介電強度 | 1.6mm | ASTM D-149 | 41 | Kv/mm | |
| 損耗因數 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 0.001 | ||
| 介電常數 | 3.2mm(0.125in) | ASTM D-150 | 3.6 | ||
| 損耗因數 | 0.8mm(0.032in) | ASTM D-150 | 0.029 | ||
| 損耗因數 | 0.8mm(0.032in) | ASTM D-150 | 0.009 | ||
| 損耗因數 | 3.2mm(0.125in) | ASTM D-150 | 0.013 | ||
| 介電常數 | 0.8mm(0.032in) | ASTM D-150 | 3.3 | ||
| 表面電阻率 | ASTM D-257 | >1×1016 | Ohm | ||
| 介電常數 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 3.9 | ||
| 介電常數 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 4.1 | ||
| 體積電阻率 | ASTM D-257 | >1×1016 | Ohm-cm | ||
| 損耗因數 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 0.002 | ||
| 損耗因數 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 0.002 | ||
| 損耗因數 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 0.001 | ||
| 介電常數 | 3.2mm(0.125in) | ASTM D-150 | 3.2 | ||
| 介電常數 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 3.9 | ||
| 損耗因數 | 3.2mm(0.125in) | ASTM D-150 | 0.028 | ||
| 加工性能 | 損耗因數 | 3.2mm(0.125in) | ASTM D-150 | 0.008 | |
| 熱性能 | 熱變形溫度 | 1.80MPa | ASTM D-648 | 239 | ℃ |
| 玻璃化轉變溫度 | ASTM D-3418 | 120 | ℃ | ||
| 模壓溫度范圍 | 30-95 | ℃ | |||
| 干燥溫度 | 135 | ℃ | |||
| 熔點 | ASTM D-3418 | 335 | ℃ | ||
| 解鏈溫度范圍 | 350-360 | ℃ | |||
| 其它性能 | 工業含水量 | <0.01 | % | ||
| RTI,Electrical | 1.5mm | UL 746-B | 130 | ℃ | |
| RTI,Mechanical with Impact | 1.5mm | UL 746-B | 130 | ℃ | |
| RTI,Mechanical without Impact | 1.5mm | UL 746-B | 130 | ℃ | |